It was suddenly cooled in brine in heat treatment, this is the main reason for the component to crack after heat treatment.
3) A given component cracked after heat treatment. What can be the possible reason ?
Answer is:
It was suddenly cooled in brine
Explanation:
Related Heat Treatment MCQ with Answers
Answer is:
Low-carbon steel parts
Explanation:
Case-hardening or surface hardening is the process of hardening the surface of a metal object while allowing the metal deeper underneath to remain soft, thus forming a thin layer of harder metal (called the "case") at the surface.
Normally Low carbon steel parts are subjected to case hardening process.
5) To reduce internal stresses of a hardened tool, the method of heat treatment generally applied is
Answer is:
Tempering
Explanation:
The tempering process consists of heating the hardened steel to the appropriate tempering temperature and soaking at this temperature, for a definite period.
Answer is:
Tempering
Explanation:
The tempering process consists of heating the hardened steel to the appropriate tempering temperature and soaking at this temperature, for a definite period.
Answer is:
Nitriding
Explanation:
In the nitriding process, the surface is enriched not with carbon, but with nitrogen. There are two systems in common use, gas nitriding and salt bath nitriding.